1. The longitudinal tear in the middle of the steel belt is 14-15 meters, how to repair it?
The upper and lower covering glue of the damaged part can be peeled off (the length exceeds the damaged part by 50-100mm, and the width exceeds the damaged part by 30-50mm), and at the same time, take a piece of rubber with the same size as the peeled part (preferably with a layer of cloth), and then It can be repaired according to the cold glue method.
2. Comparison of EP high temperature resistant belt and cotton canvas high temperature resistant belt:
a. The same point: the surface covering glue is the same.
b. Differences: cotton canvas can withstand a maximum temperature of 150 degree ; EP-TNG canvas can be used for a long time at 200 degree , and can be used at a maximum of 220 degree ;
The strength of cotton canvas is relatively low, only 50N/mm; while the strength of EP-TNG canvas is relatively high, and the commonly used type 200 is 200N/mm;
Viðloðun bómullarstriga með háhitaþolnu belti er tiltölulega lágt og viðloðun EP háhitaþolna beltisins er tiltölulega hátt; endingartími EP háhitaþolna beltisins er augljóslega lengri en bómullarstriga með háhitaþolnu belti.
3. Hot glue stripping method (is it good to remove the glue at one end)?
Þetta er önnur aðferð við að líma, þessi aðferð er líka möguleg, en ef þú notar þessa aðferð skaltu fylgjast með eftirfarandi atriðum:
a. Be sure to use sealing glue;
b. The parts where the edge rubber parts meet must be connected by vulcanized rubber;
c. The parts where the rubber is connected must be polished
The disadvantage is that the edge glue part is easily damaged if it is not handled properly.
4. The joint temperature reaches 120 degree , but does not reach the normal vulcanization temperature?
no. The normal vulcanization and crosslinking temperature of rubber is determined by the vulcanizing agent and accelerator in the rubber. In order to ensure the safety of rubber processing, the general manufacturer will not set the vulcanization starting temperature of the rubber used in the conveyor belt to be very low. Therefore, when the temperature reaches 120 degree , the rubber will not enter the normal vulcanization state. Therefore, at 120 degree , the quality of the conveyor belt joint will be greatly affected.
Venjulega, þegar vökvunarhitastigið er hærra en mikilvæga vökvunarhitastig eldsneytis og vökunarefnis og getur ekki náð eðlilegu vökunarhitastigi, er hægt að nota aðferðina til að lengja vökvunartímann til að gera vúlkun gúmmísins uppfylla kröfurnar. Yfirleitt, í hvert sinn sem hitastigið er lægra en 10 gráður, lengist vúlkaneringartíminn um 2-4 sinnum. Auðvitað, af frammistöðuástæðum, mælum við ekki með notkun lágs-hitastigs og langvarandi eldvirkni.
5. Can core rubbers from different manufacturers be mixed?
Ekki er mælt með því að blanda kjarnagúmmíi frá mismunandi framleiðendum vegna þess að formúlan af kjarnagúmmíi frá mismunandi framleiðendum er mismunandi. Það eru margar tegundir af efnablöndur í gúmmíi og sum þeirra hafa gagnvirk viðbrögð. Í formúlu sama framleiðanda verða engin efnablöndur með skaðleg gagnvirk viðbrögð, en formúlur mismunandi framleiðenda eru mjög mismunandi. Þegar það er notað getur verið gagnvirk endurspeglun efnablöndur, sem hefur áhrif á notkun kjarnagúmmísins.